Scientists know how to predict formation of gas pockets in 3D printing process

Google+ Pinterest LinkedIn Tumblr +

 

During the Additive Manufacturing process, if gas trapped inside the metal powders that feed the 3D printers, microscopic gas pockets could appear. These regions have Swiss-cheese-like structures and are less dense and weaker than their surroundings, and can lead to cracks and other failures.

Argonne scientists in front of a specialty system that can simulate the Laser Powder Bed Fusion Process in a commercial 3D printer. Credits: Argonne National Laboratory

Research teams from Carnegie Mellon University and the U.S. Department of Energy‘s (DOE) Argonne National Laboratory has identified these gas pockets and created a methodology to predict the formation of the gas pockets. This information could dramatically improve the additive manufacturing process. Their research is published last week in Science.

The research in this paper will translate into better quality and better control in working with the machines,…”, “For additive manufacturing to really take off for the majority of companies, we need to improve the consistency of the finished products. This research is a major step in that direction.”

.Anthony Rollett, Professor at Carnegie Mellon University and an author on the paper.

The scientists used the extremely bright, high-energy X-rays at Argonne’s Advanced Photon Source (APS), a DOE Office of Science User Facility, to take super-fast video and images of a process called Laser Power Bed Fusion (LPBF), in which lasers are used to melt and fuse material powder together.

The lasers, which scan over each layer of powder to fuse metal where necessary, literally create the finished product from the ground up. When tiny gas pockets become trapped into these layers, Defects can form. The defects can cause imperfections that could lead to cracks or other breakdowns in the final product.

Until now, manufacturers did not know much about how the laser drills into the metal, creating cavities called “vapor depressions.”

However, they assumed that the fault lies in the type of metal powder or the strength of laser. As a result, manufacturers have been using a trial and error approach with different types of metals and lasers to seek to reduce the defects. In fact, the research shows that these vapor depressions exist under nearly all conditions in the process, no matter the laser or metal. Even more important, the research shows how to predict when a small depression will grow into a big and unstable one that can potentially create a defect.

“We’re drawing back the veil and revealing what’s really going on,…”, “…Most people think you shine a laser light on the surface of a metal powder, the light is absorbed by the material, and it melts the metal into a melt pool. In actuality, you’re really drilling a hole into the metal.”

-Anthony Rollett-

The Argonne National Labs Advanced Photon Source facility. Image: Carnegie Mellon University

By using one of the most powerful synchrotron facilities in the world at Argonne’s APS, the researchers observed, researchers watched what happens as the laser moves across the metal powder bed to create each layer of the product.

The melt pool shape, under perfect conditions, is shallow and semicircular, called the “conduction mode.” But during the actual printing process, the high-power laser, often moving at a low speed, can change the melt pool shape to something like a keyhole in a warded lock: round and large on top, with a narrow spike at the bottom. Such “keyhole mode” melting can potentially lead to defects in the final product.


The photo above, taken under the synchrotron at Argonne National Laboratory, shows a keyhole void about to be formed during the metal 3-D printing process. During laser powder bed fusion, a 3-D printer “drills” a hole into the metal. Image:Carnegie Mellon University

The research shows that keyholes form when a certain laser power density is reached that is sufficient to boil the metal. This, in turn, reveals the critical importance of the laser focus in the additive manufacturing process, an element that has received scant attention so far, according to the research team.

The keyhole phenomenon was able to be viewed for the first time with such details because of the specialized capability developed at Argonne,…”, “Of course, the intense high-energy X-ray beam at the APS is the key.”

.Tao Sun, an Argonne physicist and an author on the paper.

The research team believes this research could motivate makers of additive manufacturing machines to offer more flexibility when controlling the machines and that the improved use of the machines could lead to a significant improvement in the final product.

“It’s important because 3D printing, in general, is rather slow,…”, “It takes hours to print a part that is a few inches high. That’s OK if you can afford to pay for the technique, but we need to do better.”

-Anthony Rollett-

Find More Additive Manufacturing Industry News
on

additivenews.com

additive manufacturing newsletter

Sources & More information

Related article categories:
Industry

Article and featured image:

Source: The article was gently conceded by Roboze and was re-edited by João Andrade on Feb28, 2019;

Share.
Additive Manufacturing

FREE
VIEW